210mm High Carbon Chef Knife

0.00
sold out

#87

European style chef knife in differentially heat treated carbon steel. This is a very light knife and a great all round knife. One of my favorites.
Not being stainless it is not for everyone as it requires more care in order to develop a nice patina, rather than to rust. If well maintained it is a great knife, with a steel that is easy to sharpen.

 

Weight: 210g

Balance point: Between the bolster and the logo.

Blade

The blade has a convex grind and is tapered from the bolster to the tip. The thickness right behind the secondary bevel is 0.1-0.2mm

The spine and choil has been rounded to make the knife comfortable to use with a pinch grip.

 

Steel: 1095 high carbon steel

1095 has been a very popular high-carbon steel for knives for many years. It holds a great edge and is very easy to sharpen, but rusts easily if not cared for.

 

Heat treatment: The blade has been differentially heat treated inhouse in a PID controlled furnace at 815°C and quenched in fast specialty quenching oil. Finally it is tempered in a PID controlled oven to the final hardness.

The differential hardening of the blade is produced by covering part of the blade in clay during heat treat and results in a soft spine but a hard edge. What is called a hamon in Japanese sword making.

 

Hardness: 62 HRC

Height at heel: 52mm

Thickness at

  • Spine at bolster: 2.6mm

  • Spine halfway: 2.1mm

  • 1 cm from the tip: 0.5mm

 

Handle

Material: Stabilized spalted beech.

Bolster and spacers: Stainless 303 bolster pinned to the blade with 303 pins, G10 and stainless spacers.

Add To Cart

#87

European style chef knife in differentially heat treated carbon steel. This is a very light knife and a great all round knife. One of my favorites.
Not being stainless it is not for everyone as it requires more care in order to develop a nice patina, rather than to rust. If well maintained it is a great knife, with a steel that is easy to sharpen.

 

Weight: 210g

Balance point: Between the bolster and the logo.

Blade

The blade has a convex grind and is tapered from the bolster to the tip. The thickness right behind the secondary bevel is 0.1-0.2mm

The spine and choil has been rounded to make the knife comfortable to use with a pinch grip.

 

Steel: 1095 high carbon steel

1095 has been a very popular high-carbon steel for knives for many years. It holds a great edge and is very easy to sharpen, but rusts easily if not cared for.

 

Heat treatment: The blade has been differentially heat treated inhouse in a PID controlled furnace at 815°C and quenched in fast specialty quenching oil. Finally it is tempered in a PID controlled oven to the final hardness.

The differential hardening of the blade is produced by covering part of the blade in clay during heat treat and results in a soft spine but a hard edge. What is called a hamon in Japanese sword making.

 

Hardness: 62 HRC

Height at heel: 52mm

Thickness at

  • Spine at bolster: 2.6mm

  • Spine halfway: 2.1mm

  • 1 cm from the tip: 0.5mm

 

Handle

Material: Stabilized spalted beech.

Bolster and spacers: Stainless 303 bolster pinned to the blade with 303 pins, G10 and stainless spacers.